Thermomechanical properties of coated PLA-3D-printed orthopedic plate with PCL/Akermanite nano-fibers: Experimental procedure and AI optimization

分类： 机械工程 >> 机械工程其他学科 提交时间： 2024-04-02

X Zhang S. Mohammad Sajadi Omid Malekahmadi Z Li Nidal H. Abu-Hamdeh Muhyaddin J. H. Rawa Meshari A. Al-Ebrahim Aliakbar Karimipour HPM Viet

摘要： In this study, first, an orthopedic plate was 3D printed with Polylactic acid (PLA) and coated with polycaprolactone (PCL)/Akermanite (AKT) nano-fibers. The composition included 8 wt.% of PCL and 3 wt.% of nAKT, while diameter of the PCL/AKT nano-fibers was approximately 253 nm ± 33 nm. Thermomechanical properties such as pressure, three-point bending flexural, and thermal conductivity of coated and non-coated specimens were examined and compared. In the next step, the bioactivity of the coated samples was evaluated following a 28-day immersion in simulated body fluid (SBF). Further, scanning electron microscope (SEM) images were taken to assess morphology of nanofibers and apatite formation on samples. By adding PCL to PLA, the maximum pressure force is enhanced by 16.83%. Further by adding nAKT to PLA+PCL sample, the maximum pressure force is enhanced by 4.72%. Further, by adding PCL to PLA, the maximum bending flexural force is enhanced by 21.06%. Further by adding nAKT to PLA+PCL sample, the maximum bending flexural force is enhanced by 21.39%. The results of this study are used to improve modeling of the orthopedic plates.

通过

 点击量 390  下载量 106  评论